Ibhola yeCeramic ephakathi yeAlumina yokupakisha kunye nokugaya
Ibhola yeCeramic ephakathi yeAlumina yokupakisha kunye nokugaya
1) Iibhola (iibhola) okanye iisilinda
2) Inkxaso egqwesileyo kakhulu kunye neendaba ezigubungelayo
3) Umsebenzi njengenkxaso yemithombo yeendaba kwiibhedi ze-catalyst okanye ezinye iibhedi zeekhemikhali kwi-reactors okanye iinqaba.
4) Ukusebenza okuhle kakhulu kunye nokuzinza kwi-asidi kunye nezinye iindawo ezingqongileyo zeekhemikhali
I-5) Uzinzo oluhle kakhulu lweekhemikhali kunye nezinga eliphantsi lokufunxa kwamanzi
6) Inokumelana noxinzelelo oluphezulu kunye nokushisa okuphezulu
7) Inokusetyenziswa nakwinkonzo ye-caustic eshushu kuba inokuxhathisa ngaphezu kwe-10% yenkonzo ye-sodium hydroxide ukuya kuma-60ºC, kunye ne-1% yenkonzo ye-sodium hydroxide yobushushu ukuya kwi-100ºC.
I-8) Iyakwazi ukumelana nokubola kweekhemikhali zayo nayiphi na i-asidi (kubandakanywa ne-organic kunye ne-inorganic acids, kodwa ngaphandle kwe-HF acid), uninzi lwe-alkali kunye ne-solvent organic
9) Iya kwandisa abasasazi bolwelo kunye negesi, ixhase kwaye ikhusele i-catalyst kwaye igweme ityhefu.
| Al2O3+SiO2 | Al2O3 | Fe2O3 | MgO | K2O+Na2O +CaO | Abanye |
| > 93% | >50% | <1% | <0.5% | <4% | <1% |
| Into | Ixabiso |
| Ukufunxwa kwamanzi (%) | <2 |
| Ubuninzi bobuninzi (g/cm3) | 1.4-1.5 |
| Umxhuzulane okhethekileyo (g/cm3) | 2.4-2.6 |
| Umthamo wasimahla (%) | 40 |
| Ubushushu bokusebenza.(ubuninzi) (℃) | 1200 |
| Ubunzima bukaMoh (isikali) | >7 |
| Ukumelana neAcidi (%) | >99.6 |
| Ukuxhathisa kwealkali (%) | >85 |
| Ubungakanani | Amandla okutyumza | |
| Kg/isuntswana | KN/isuntswana | |
| 1/8''(3mm) | >560 | >0.56 |
| 3/8''(10mm) | >1500 | >1.5 |
| 1/2''(13mm) | >1650 | >1.65 |
| 3/4''(19mm) | >2890 | >2.89 |
| 1''(25mm) | > 4890 | >4.89 |